Kunshan sandblasting processing scope: Hardware derusting, aluminum alloy sandblasting, glass sandblasting (fogging effect), plastic sandblasting (deburring), acrylic sandblasting (fogging effect), PC, PS surface treatment, resin surface treatment, casting workpiece sandblasting, zinc alloy sandblasting (rough surface), stainless steel sandblasting, stone sandblasting, hardware depaining, hardware welding scar removal, shot blasting, etc Surface treatment of accessories.

Acrylic sandblasting: if the customer requires very foggy, generally spray glass sand. If the requirement is higher, white corundum can be selected. If the requirements are not very foggy and have certain transparency, glass beads must be selected. Sometimes a little glass sand will be added into the glass beads, so that the effect of spraying out is a little transparent.

Stainless steel sandblasting: generally need to know what kind of stainless steel panel is, there are polished surface, alloy steel shot, wire drawing surface, as well as the fog surface of the original plate. If roughness is required, brown corundum and white corundum can be selected. If there are special requirements, if smooth, glass beads and glass sand can be selected.

Die casting parts: generally, low alloy steel is deburred. Generally, shot blasting machine can be used for low alloy steel. Cast steel ball and steel ball are used for sand blasting. The surface scratch of the object is less and the scratch is shallow and small. For the thick surface dirt removal, steel sand can be used together. If you want to make the color of sandblasted aluminum parts whiter, you should consider the cost of use

For high stainless steel shot and steel wire cut shot, if you want to save cost, consider casting steel ball and continuous steel ball at the ratio of 8:2. When sandblasting and shot blasting, the steel ball will be cleaned once every time, and more sandblasting and shot blasting can also achieve a white effect.

Iron parts: Generally speaking, the process of sandblasting iron parts is to remove oxide layer and rust, and to remove edge burrs. Some of them will electroplate low alloy steel after spraying sand, and some will apply paint after spraying sand. Generally, brown corundum and white corundum are sprayed (selected according to color demand and economic cost).